C0402C120J3GAC9028
| Model | C0402C120J3GAC9028 |
| Description | Ceramic Capacitor, Multilayer, Ceramic, 25V, 5% +Tol, 5% -Tol, C0G, -/+30ppm/Cel TC, 0.000012uF, 0402, |
| PDF file | Total 19 pages (File size: 1011K) |
| Chip Manufacturer | KEMET |
Surface Mount Multilayer Ceramic Chip Capacitors (SMD MLCCs) – C0G Dielectric, 10VDC-200VDC (Commercial Grade)
Soldering Process
Recommended Soldering Technique:
• Solder wave or solder reflow for EIA case sizes 0603, 0805 and 1206
• All other EIA case sizes are limited to solder reflow only
Recommended Soldering Profile:
• KEMET recommends following the guidelines outlined in IPC/JEDEC J-STD-020
Table 4 – Performance & Reliability: Test Methods and Conditions
Stress
Terminal Strength
Board Flex
Reference
JIS-C-6429
JIS-C-6429
Test or Inspection Method
Appendix 1, Note: Force of 1.8kg for 60 seconds.
Appendix 2, Note: 2mm (min) for all except 3mm for C0G.
Magnification 50 X. Conditions:
Solderability
J-STD-002
a) Method B, 4 hours @ 155°C, dry heat @ 235°C
b) Method B @ 215°C category 3
c) Method D, category 3 @ 260°C
Temperature Cycling
Biased Humidity
Moisture Resistance
Thermal Shock
High Temperature Life
Storage Life
Mechanical Shock
Resistance to Solvents
JESD22 Method JA-104
MIL-STD-202 Method 103
MIL-STD-202 Method 106
MIL-STD-202 Method 107
MIL-STD-202 Method 108
/ EIA -198
MIL-STD-202 Method 108
MIL-STD-202 Method 213
MIL-STD-202 Method 215
1000 Cycles (-55°C to +125°C), Measurement at 24 hours. +/- 2 hours after test conclusion.
Load Humidity: 1000 hours 85°C/85%RH and Rated Voltage. Add 100K ohm resistor. Measurement
at 24 hours. +/- 2 hours after test conclusion.
Low Volt Humidity: 1000 hours 85°C/85%RH and 1.5V. Add 100K ohm resistor.
Measurement at 24 hours. +/- 2 hours after test conclusion.
t = 24 hours/cycle. Steps 7a & 7b not required. Unpowered.
Measurement at 24 hours. +/- 2 hours after test conclusion.
-55°C/+125°C. Note: Number of cycles required-300, Maximum transfer time-20 seconds, Dwell
time-15 minutes. Air-Air.
1000 hours at 125°C (85°C for X5R, Z5U and Y5V) with 2 X rated voltage applied.
150°C, 0VDC, for 1000 Hours.
Figure 1 of Method 213, Condition F.
Add aqueous wash chemical - OKEM Clean or equivalent.
Storage and Handling
Ceramic chip capacitors should be stored in normal working environments. While the chips themselves are quite robust in other
environments, solderability will be degraded by exposure to high temperatures, high humidity, corrosive atmospheres, and long term
storage. In addition, packaging materials will be degraded by high temperature – reels may soften or warp, and tape peel force may
increase. KEMET recommends that maximum storage temperature not exceed 40ºC, and maximum storage humidity not exceed
70% relative humidity. In addition, temperature fluctuations should be minimized to avoid condensation on the parts, and atmospheres
should be free of chlorine and sulfur bearing compounds. For optimized solderability, chip stock should be used promptly, preferably
within 1.5 years of receipt.